JLS Launchs Innovative Alternatives to Sb2O3 for ABS

JLS-MB600

Appearance Pellets

The Key Advantages

Table 1 Properties of FRABS with MB600

ABS, %wt		Flame Retardant, %wt		UL94 1.6mm	MI (220℃,10kg) g/10min	Tensile Strength MPa	Flexural ModulusMPa	Flexural Strength MPa	Charpy Notched Impact StengthKJ/m2
KF-718*	KF-730*	FR245	MB600	UL94 1.6mm	MI (220℃,10kg) g/10min	Tensile Strength MPa	Flexural ModulusMPa	Flexural Strength MPa	Charpy Notched Impact StengthKJ/m2
100	/	/	/	HB	10	40.0	1900	60.0	35.0
/	100	/	/	HB	20	47.0	2500	76.0	20.0
36	36	18	10	V0	54	41.0	2363	66.3	18.5
48	24	18	10	V0	52	40.7	2354	66.8	20.2

*KF-718 and KF-730 are ABS from KINGFA China

Table 2 Properties of FRABS with MB600 and ABS Powders

ABS, %wt		Flame Retardant, %wt		UL94 1.6mm	MI (220℃,10kg) g/10min	Tensile Strength MPa	Flexural ModulusMPa	Flexural Strength MPa	Charpy Notched Impact StengthKJ/m2
PA-757**	HR-181***	FR245	MB600	UL94 1.6mm	MI (220℃,10kg) g/10min	Tensile Strength MPa	Flexural ModulusMPa	Flexural Strength MPa	Charpy Notched Impact StengthKJ/m2
100	/	/	/	HB	22	45.0	2650	76.0	20.0
67	5	18	10	V0	53	42.0	2378	68.6	15.1
63	8	19	10	V0	47	40.4	2254	66.7	17.9

**PA757: ABS from CHIMEI

***HR-181: ABS powder(High rubber content) from Korea Kumho

Note: 0.15%-0.20% PTFE is required for above formula

Regulatory compatibility

REACH, RoHS



YOUR LOCATION : HOME>PRODUCTS>HFFR* POWDERS

Share To

Contact

Product Informations

PRODUCTS

CONTACT US

A kind of masterbatch based on Phosphorus-nitrogen (P/N) flame retardant that is antimony-free, can completely replace Sb₂O₃ in order to meet UL94 V0 and notched Izod impact. JLS-MB600 can reduce dependence on Sb₂O₃ as well as allow compliance with California Bill 65 and European TCO regulations.

Innovative Antimony Replacement in ABS